The Interface of TiB₂ and Al₃Ti in Molten Aluminum

In the grain refinement of aluminum, Al₃Ti and TiB₂ particles are introduced to reduce the casting grain size down to 200 micrometer level, which makes cold working possible. The particles are brought in by the addition of Al-Ti-B-type master alloys. It is generally believed that TiB₂ particles are stable and nucleate α-Al grains in solidification in the presence of titanium in solution from the dissolution of Al₃Ti particles in the master alloys. The titanium in solution either forms Al₃Ti layers on the surface of TiB₂ particles to promote the nucleation of α-Al grains or remains as solute to restrict the growth of α-Al grains in solidification. However, a consensus on a grain refinement mechanism is still to be reached due to the lack of direct observation of the three phases in castings. This paper presents finding of the TiB₂/Al₃Ti interfaces in an Al-Ti-B master alloy. It demonstrates a strong epitaxial growth of Al₃Ti on the surface of TiB₂ particles, a sign of the formation of an Al₃Ti layer on the surface of TiB₂ particles in grain refinement practice. The Al₃Ti layer has a crystal coherency with α-Al and hence offers a substrate for heterogeneous nucleation of α-Al grains. However, the layer must be dynamic to avoid the formation of compounded Al₃Ti and TiB₂ particles leading to the loss of efficiency in grain refinement.